Pre-Pregnated Carbon Cloth Engineering Properties

Engineering Materials

Pre-Pregnated Carbon Cloth Engineering Properties Imperial Units

Description
Hot Wet
Hot
RT
Cold
Minimum
(160F, 95% RH)
(160F)
(75F)
(-65F)
F tu1 (psi)
86297
82817
79771
73969
73969
E t11 (psi)
7702519
7702519
7702519
7702519
7702519
F tu2 (psi)
70488
70198
66427
63091
63091
E t22 (psi)
7702519
7702519
7702519
7702519
7702519
v 12
0.06
0.06
0.06
0.06
0.06
F cu1 (psi)
52069
69328
86442
92244
52069
E c11 (psi)
7702519
7702519
7702519
7702519
7702519
F cu2 (psi)
48298
62946
77885
83252
48298
E c22 (psi)
7702519
7702519
7702519
7702519
7702519
F su12 (psi)
11168
13198
17405
20015
11168
G 12 (psi)
559991
559991
559991
559991
559991
ILS
-
-
8023
-
8023
Thickness (in)*
0.0086
0.0086
0.0086
0.0086
-
E av11 (psi)
7702519
7702519
7702519
7702519
7702519
E av22 (psi)
7702519
7702519
7702519
7702519
7702519
CAI Compression Strain
3000.0
3994.4
4980.5
5314.8
3000.0
Filled Hole Tension Strain
4500.0
4318.5
4159.7
3857.1
3857.1
Open Hole Tension Stress (psi)
-
-
-
-
-
Open Hole Compression Stress (psi)
23699
-
39682
-
23699
Filled Hole Tensions Stress (psi)
-
-
42235
-
42235
Filled Hole Compression Stress (psi)
36956
-
-
-
36956
50% Bypass Tension Stress (psi)
-
-
100308
-
100308
50% Bypass Compression Stress (psi)
-
-
102730
-
102730
25% Bypass Tension Stress (psi)
-
-
118829
-
118829
25% Bypass Compression Stress (psi)
-
-
186939
-
186939
Single Shear Bearing Stress (psi)
81352
-
106371
-
81352
Double Shear Bearing (psi)
44904
-
77421
-
44904
* Check Thickness Values against specific project material
Contribute Article
Spider Optimizer

© Copyright 2000 - 2017, by Engineers Edge, LLC www.engineersedge.com
All rights reserved
Disclaimer | Feedback | Advertising | Contact


User Reviews/Comments:

There are currently no comments available.


Add a Comment (you must be logged in to post comment Register):
Name:
Email: (Optional)
Comment: