Engineering Properties Common Composite Laminates

Engineering Materials

Wet Laminate Carbon Cloth engineering properties in both SI and imperial units.

Wet Laminate Carbon Cloth Engineering Data SI Units

Description
Hot Wet
Hot
RT
Cold
Minimum
(160F, 95% RH)
(160F)
(75F)
(-65F)
-
Ftu 1 (Mpa)
622.0
676.0
725.0
762.0
622.0
E t11 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
Ftu 2 (Mpa)
527.0
671.0
684.0
722.0
527.0
E t22 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
v 12 (Mpa)
0.030
0.030
0.030
0.030
0.030
Fcu 1 (Mpa)
378.0
451.0
518.0
520.0
378.0
E c11 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
Fcu 2 (Mpa)
350.0
418.0
480.0
480.0
350.0
E c22 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
Fsu 12 (Mpa)
49.0
58.0
67.0
79.0
49.0
G 12 (Mpa)
2700.0
2700.0
2700.0
2700.0
2700.0
ILS
-
-
38.0
47.0
38.0
Thickness (mm)*
0.24
0.24
0.24
0.24
-
E av11 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
E av22 (Mpa)
60000.0
60000.0
60000.0
60000.0
60000.0
CAI Compression Strain
3000.0
3579.4
4111.1
4127.0
3000.0
Filled Hole Tension Strain
4500.0
4890.7
5245.2
5512.9
4500.0
Open Hole Tension Stress (Mpa)
-
-
-
-
-
Open Hole Compression Stress (Mpa)
147.1
-
246.2
-
147.1
Filled Hole Tensions Stress (Mpa)
-
-
262.1
-
262.1
Filled Hole Compression Stress (Mpa)
229.3
-
-
229.3
50% Bypass Tension Stress (Mpa)
-
-
622.4
-
622.4
50% Bypass Compression Stress (Mpa)
-
-
637.5
-
637.5
25% Bypass Tension Stress (Mpa)
-
-
737.4
-
737.4
25% Bypass Compression Stress (Mpa)
-
-
1160.0
-
1160.0
Single Shear Bearing Stress (Mpa)
504.8
-
660.1
-
504.8
Double Shear Bearing (Mpa)
278.6
-
480.4
-
278.6

* Check Thickness Values against specific project material


Wet Laminate Carbon Cloth Engineering Data Imperial Units

Description
Hot Wet
Hot
RT
Cold
Minimum
(160F, 95% RH)
(160F)
(75F)
(-65F)
-
F tu1 (psi)
8702264
8702264
8702264
8702264
8702264
E t11 (psi)
435113
519143
596266
598568
435113
F tu2 (psi)
652670
709332
760749
799573
652670
E t22 (psi)
0
0
0
0
0
v 12
0.030
0.030
0.030
0.030
0
F cu1 (psi)
0
0
38011
0
0
E c11 (psi)
33260
0
0
0
0
F cu2 (psi)
0
0
90277
0
0
E c22 (psi)
0
0
92457
0
0
F su12 (psi)
0
0
106946
0
0
G 12 (psi)
0
0
168245
0
0
ILS
-
-
95734
0
0
Thickness (in)*
10.9701
0.0000
18.9142
0.0000
-
E av11 (psi)
0
0
0
0
0
E av22 (psi)
0
0
0
0
0
CAI Compression Strain
0.0
0.0
-
0.0
0
Filled Hole Tension Strain
0.0
0.0
-
0.0
0
Open Hole Tension Stress (psi)
-
-
-
-
-
Open Hole Compression Stress (psi)
0
-
-
-
-
Filled Hole Tensions Stress (psi)
-
-
-
-
-
Filled Hole Compression Stress (psi)
0
-
-
-
0
50% Bypass Tension Stress (psi)
-
-
0
-
0
50% Bypass Compression Stress (psi)
-
-
0
-
0
25% Bypass Tension Stress (psi)
-
-
0
-
0
25% Bypass Compression Stress (psi)
-
-
0
-
0
Single Shear Bearing Stress (psi)
0
-
0
-
0
Contribute Article
Spider Optimizer

© Copyright 2000 - 2017, by Engineers Edge, LLC www.engineersedge.com
All rights reserved
Disclaimer | Feedback | Advertising | Contact


User Reviews/Comments:

There are currently no comments available.


Add a Comment (you must be logged in to post comment Register):
Name:
Email: (Optional)
Comment: